| 规格级别 | 其它 其它 玻纤增强 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | 30%玻纤增强 | ||
| 加工条件 |
③原料技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 比重 | --- | ASTM D-792 | 1.53 | --- | |
| 机械性能 | 拉伸强度 | --- | ASTM D-638 | 132 | MPa | |
| IZOD冲击强度 | 缺口 | --- | ASTM D-256 | 93 | J/m | |
| 反蜗缺口 | --- | ASTM D-256 | 530 | J/m | ||
| 拉伸伸长 | --- | ASTM D-638 | 2.5 | --- | ||
| 弯曲模量 | --- | ASTM D-790 | 9.120 | MPa | ||
| 弯曲强度 | --- | ASTM D-790 | 210 | MPa | ||
| 电气性能 | 体积电阻率 | 3mmt | ASTM D-257 | 5×1016 | Ω.cm | |
| 绝缘破坏强度 | 短时：3mmt | ASTM D-149 | 23 | MV/M | ||
| 热性能 | 线性膨胀系数 | 室温 | --- | 2-7 | ×10-5/℃ | |
| 热变形温度 | 1.82MPa | ASTM D-648 | 213 | ℃ | ||
| 阻燃性 | --- | UL 94 | HB | --- | ||
| 其它性能 | 带电半衰期 | 20℃，65%RH | --- | >300 | S | |
| UL认定温度 | 带冲击 | --- | --- | 130 | ℃ | |
| 无冲击 | --- | --- | 140 | ℃ | ||
| 表面电阻率 | --- | --- | 6×1016 | Ω | ||
| UL认定温度 | 电气的 | --- | 130 | ℃ | ||
| UL认定耐电弧电阻 | *2 | --- | 500 | V | ||
| UL认定耐电弧性 | *2 | --- | 125 | S | ||